Semiconductor devices with field plates

ABSTRACT

A III-N device is described with a III-N material layer, an insulator layer on a surface of the III-N material layer, an etch stop layer on an opposite side of the insulator layer from the III-N material layer, and an electrode defining layer on an opposite side of the etch stop layer from the insulator layer. A recess is formed in the electrode defining layer. An electrode is formed in the recess. The insulator can have a precisely controlled thickness, particularly between the electrode and III-N material layer.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No. 13/748,907, filed Jan. 24, 2013, which is a divisional of U.S. application Ser. No. 12/550,140, filed Aug. 28, 2009, now U.S. Pat. No. 8,390,000. The disclosures of the prior applications are considered part of and are incorporated by reference in the disclosure of this application.

TECHNICAL FIELD

This invention relates to semiconductor electronic devices, specifically devices with field plates.

BACKGROUND

To date, modern power semiconductor devices, including devices such as power MOSFETs and Insulated Gate Bipolar Transistors (IGBT), have been typically fabricated with silicon (Si) semiconductor materials. More recently, silicon carbide (SiC) power devices have been researched due to their superior properties. III-Nitride (III-N) semiconductor devices are now emerging as an attractive candidate to carry large currents and support high voltages, and provide very low on resistance, high voltage device operation, and fast switching times. A typical III-N high electron mobility transistor (HEMT), shown in FIG. 1, comprises a substrate 10, a channel layer 11, such as a layer of GaN, atop the substrate, and a barrier layer 12, such as a layer of Al_(x)Ga_(1-x)N, atop the channel layer. A two-dimensional electron gas (2DEG) channel 19 is induced in the channel layer 11 near the interface between the channel layer 11 and the barrier layer 12. Source and drain electrodes 14 and 15, respectively, form ohmic contacts to the 2DEG channel. Gate 16 modulates the portion of the 2DEG in the gate region, i.e., directly beneath gate 16.

Field plates are commonly used in III-N devices to shape the electric field in the high-field region of the device in such a way that reduces the peak electric field and increases the device breakdown voltage, thereby allowing for higher voltage operation. An example of a field plated III-N HEMT is shown in FIG. 2. In addition to the layers included in the device of FIG. 1, the device in FIG. 2 includes a field plate 18 which is connected to gate 16, and an insulator layer 13, such as a layer of SiN, is between the field plate and the barrier layer 12. Field plate 18 can include or be formed of the same material as gate 16. Insulator layer 13 can act as a surface passivation layer, preventing or suppressing voltage fluctuations at the surface of the III-N material adjacent to insulator layer 13.

Slant field plates have been shown to be particularly effective in reducing the peak electric field and increasing the breakdown voltage in III-N devices. A III-N device similar to that of FIG. 2, but with a slant field plate 28 is shown in FIG. 3. In this device, gate 16 and slant field plate 28 are formed of a single electrode 29. Insulator layer 23, which can be of SiN, contains a recess which defines at least in part the shape of electrode 29. Herein, insulator layer 23 will be referred to as “electrode defining layer 23”. Electrode defining layer 23 can also act as a surface passivation layer, preventing or suppressing voltage fluctuations at the surface of the III-N material adjacent to electrode defining layer 23. The gate 16 and slant field plate 28 in this device can be formed by first depositing electrode defining layer 23 over the entire surface of barrier layer 12, then etching a recess through the electrode defining layer 23 in the region containing gate 16, and finally depositing electrode 29 at least in the recess.

In many applications in which III-N devices are used, for example high power and high voltage applications, it can be advantageous to include a gate insulator between gate 16 and the underlying III-N layers in order to prevent gate leakage. A device with a slant field plate and a gate insulator is shown in FIG. 4. This device can be achieved by a slight modification to the process for the device in FIG. 3. For the device in FIG. 4, the recess in electrode defining layer 23 is only etched part way through the layer (rather than all the way through the layer), after which electrode 29 is deposited. In this device, the portion of electrode defining layer 23 which is between gate 16 and the underlying III-N layers serves as a gate insulator.

SUMMARY

In one aspect, a III-N device is described that includes a III-N material layer, an insulator layer on a surface of the III-N material layer, an etch stop layer on an opposite side of the insulator layer from the III-N material layer, an electrode defining layer on an opposite side of the etch stop layer from the etch stop layer from the insulator layer and an electrode. A recess is formed in the electrode defining layer and the electrode is formed in the recess.

For all devices described herein, one or more of the following may be applicable. The electrode can include a field plate. The field plate can be a slant field plate. A portion of the recess in the electrode defining layer can have angled walls with at least a portion that is at a non-perpendicular angle to a main surface of the etch stop layer, the angled walls defining the slant field plate. The non-perpendicular angle can be between about 5 degrees and 85 degrees. The insulator layer can be a passivation layer. The insulator layer can be formed of an oxide or nitride. The insulator layer can be about 2-50 nanometers thick. The insulator layer can have a capacitance per unit area of about 0.8-40 millifarads/meter². The electrode defining layer can be formed of an oxide or nitride. The electrode defining layer can be at least about 100 nanometers thick. A combined thickness of the insulator layer and the electrode defining layer can be sufficient to substantially suppress dispersion. The etch stop layer can be between about 1 and 15 nanometers thick. The etch stop layer can be formed of aluminum nitride. The electrode defining layer and etch stop layer can be formed of different materials. The etch stop layer and insulator layer can be formed of different materials. The recess can be formed in the etch stop layer.

In some embodiments, the III-N device is a diode. The diode can include one or more of the following features. The recess can be formed in the insulator layer. A first portion of the III-N material layer can have a first composition and a second portion of the III-N material layer can have a second composition, wherein a difference between the first composition and the second composition forms a 2DEG channel in the III-N material layer. The diode can include a cathode, wherein a portion of the electrode is an anode, the anode forms a substantially Schottky contact to the III-N material layer, and the cathode is in electrical contact with the 2DEG channel. The recess can extend into the III-N material layer and the electrode is in a portion of the recess in the III-N material layer. The recess can extend through the 2DEG channel. A threshold of a first region of the device can be greater than about −15V, wherein the first region comprises a portion of the device which is between an anode region and the cathode and is adjacent to the anode region. A thickness of the insulator layer can be sufficient to prevent leakage currents greater than about 10 microamperes/millimeter from passing through the insulator layer during device operation. The electrode can be an anode electrode and the device can further comprise a cathode.

In some embodiments, the device is a HEMT. The HEMT may include one or more of the following features. A first portion of the III-N material layer can have a first composition and a second portion of the III-N material layer can have a second composition, wherein a difference between the first composition and the second composition forms a 2DEG channel in the III-N material layer. The device can include source and a drain, wherein a portion of the electrode is a gate, and the source and the drain are in electrical contact with the 2DEG channel. A device threshold voltage can be greater than about −30V. A thickness of the insulator layer can be chosen such that the device threshold voltage is greater than about −30V. A thickness of the insulator layer can be sufficient to prevent leakage currents greater than about 100 microamperes from passing through the insulator layer during device operation. The electrode can be a gate electrode and the device can further comprise a source and a drain. The device can be a FET, where a dynamic on-resistance as measured when the device is switched from the OFF state, with a source-drain bias of about 800 V or less, to the ON state, is equal to or less than 1.4 times a DC on-resistance.

Any one of the devices described herein may include multiple field plates. Devices with multiple field plates can include the following features. The electrode defining layer and the etch stop layer can be a first electrode defining layer and a first etch stop layer, the device can further comprise a stack on an opposite side of the first electrode defining layer from the first etch stop layer, wherein the stack comprises a second etch stop layer and a second electrode defining layer. A recess can be formed in the stack, and a portion of the electrode overlies the stack. A second insulator layer can be between the first electrode defining layer and the second etch stop layer. The device can include a second electrode, wherein a second recess is formed in the second electrode defining layer and in the second etch stop layer, and the second electrode can be formed in the second recess. The second electrode can be electrically connected to the first electrode. The device can include a plurality of stacks, wherein a recess is formed in each stack, and an electrode is formed in each recess.

In another aspect a method of forming a III-N device is described. The method includes applying an insulator layer on the surface of a III-N material layer. After applying the insulator layer, an etch stop layer is applied on the insulator layer. After applying the etch stop layer, the electrode defining layer is applied on the etch stop layer. The electrode defining layer is etched to form the recess, wherein the recess is defined at least in part by a wall that is not perpendicular to a surface of the etch stop layer. The etching step uses an etchant that is selective to etching the electrode defining layer at a faster rate than the etch stop layer. A conductive material is deposited in the recess and on an exposed portion of the electrode defining layer.

One or more embodiments of the method can include one or more of the following features. The method can include etching the etch stop layer to extend the recess in the electrode defining layer to the insulator layer. Etching the etch stop layer can include wet etching. Etching the electrode defining layer can include dry etching or a Fluorine-based dry etch. An etch process used to etch the etch stop layer may not substantially etch the electrode defining layer or the insulator layer. The etch process can etch the etch stop layer with a selectivity of about 10:1 or higher. Etching the electrode defining layer can result in the electrode defining layer having angled walls with at least a portion that is at a non-perpendicular angle to a main surface of the etch stop layer. The non-perpendicular angle can be between about 5 degrees and 85 degrees. An etch process used to etch the electrode defining layer may not substantially etch the etch stop layer. The etch process can etch the electrode defining layer with a selectivity of about 10:1 or higher.

Gate insulators typically need to be made thin to maintain an adequate coupling between the gate and 2DEG channel, and typically the thickness of the gate insulator must be controlled to a high degree of precision in order to ensure reproducibility of the device threshold voltage and other device parameters. The techniques described here may result in sufficiently precise control of the gate insulator thickness, especially when a very thin gate insulator is required, and thus reproducible manufacturing using this process may be possible.

DESCRIPTION OF DRAWINGS

FIGS. 1-4 are schematic cross-sectional views of III-N HEMT devices of the prior art.

FIG. 5 is a schematic cross-sectional view of a III-N semiconductor transistor containing a gate insulator and a slant field plate.

FIGS. 6-11 illustrate a method of forming the III-N semiconductor transistor of FIG. 5.

FIG. 12 a is a schematic cross-sectional view of a III-N semiconductor transistor containing a gate insulator and slant field plates.

FIGS. 12 b and 12 c are graphs showing on-resistance versus drain voltage for III-N semiconductor transistors.

FIG. 13 is a schematic cross-sectional view of a III-N semiconductor transistor containing a gate insulator and slant field plates.

FIGS. 14 and 15 are schematic cross-sectional and plan views, respectively, of a III-N semiconductor diode containing a slant field plate.

FIG. 16 is a schematic cross-sectional view of a III-N semiconductor diode containing a slant field plate.

Like reference symbols in the various drawings indicate like elements.

DETAILED DESCRIPTION

Semiconductor devices, such as HEMTs and diodes, are described which can be manufactured reproducibly. The devices all include slant field plates, and some also include a gate insulator between a gate and underlying semiconductor layers. The use of slant field plates can result in devices with superior properties for high-voltage switching applications, such as high breakdown voltage and minimal dispersion at high voltage operation, while the gate insulator, when included in transistor structures, can result in reduced gate leakage. Furthermore, the manufacturing process for the devices can be reproducible using conventional semiconductor device fabrication processes. The semiconductor devices can be III-Nitride or III-N semiconductor devices, and so devices described herein include III-N semiconductor layers. Methods of forming the devices are also described.

FIG. 5 shows a schematic illustration of a III-Nitride device, i.e., a III-Nitride HEMT. As used herein, the terms III-Nitride or III-N materials, layers, devices, etc., refer to a material or device comprised of a compound semiconductor material according to the stoichiometric formula Al_(x)In_(y)Ga_(z)N, where x+y+z is about 1. The device includes a substrate layer 10, which can include or be formed of silicon, sapphire, GaN, AlN, SiC, or any other substrate suitable for use in III-N devices. In some embodiments, a substrate is not included. For example, in some embodiments the substrate is removed prior to completion of device fabrication. III-N layers 11 and 12, which are formed on top of substrate 10, are III-N materials that form the basis for the HEMT device. III-N layers 11 and 12 have different compositions, the compositions chosen such that a 2DEG channel 19 is induced in layer 11, which is hereby referred to as “channel layer 11”. Some or all of the III-N material in layer 12 has a bandgap which is larger than that of channel layer 11, so layer 12 is hereby referred to as “barrier layer 12”. In some embodiments, channel layer 11 is GaN and barrier layer 12 is Al_(x)Ga_(1-x)N, where x is between 0 and 1. It is understood that modifications to the III-N material structure can be made, as long as the resulting structure is one with which a III-N HEMT or other III-N device, such as an HFET, MISHFET, MOSFET, MESFET, JFET, CAVET, POLFET, HEMT, FET, diode, or another device can be formed. For example, additional III-N layers can also be included, such as a III-N buffer layer between the substrate 10 and the overlying III-N layers, or an AlN layer between the channel layer 11 and barrier layer 12. The III-N layers can be oriented in the [0 0 0 1] (III-face or Ga-face C-plane) polar direction, the [0 0 0 1 bar] (N-face) polar direction, or any other polar, semi-polar, or non-polar orientation. In some embodiments, the barrier layer 12 is between the substrate 10 and the channel layer 11, such as when the III-N materials are oriented in a [0 0 0 1 bar] direction or in a nitrogen-terminated semi-polar direction or in a non-polar direction. As such, while the uppermost III-N layer, i.e., the III-N layer furthest from the substrate, is shown in FIG. 5 to be the barrier layer 12, in some embodiments the uppermost III-N layer can be the channel layer 11 or another III-N layer.

The device structure can be designed such that the resulting III-N device is a depletion-mode device, such that the 2DEG channel 19 is induced in the gate region and access regions of channel layer 11 when zero voltage is applied to the gate relative to the source. Or, the III-N device can be an enhancement-mode device, such that the 2DEG channel 19 is induced in the access regions but not the gate region of channel layer 11 when zero voltage is applied to the gate relative to the source, and a positive voltage must be applied to the gate to induce a 2DEG in the gate region of channel layer 11. As used herein, the term “gate region” refers to the region in the III-N materials directly beneath gate 16, i.e. between the two vertical dashed lines in FIG. 5. The term “access regions” refers to the regions of the device which are on either side of the gate region and between the source and drain electrodes 14 and 15, respectively. Thus, the access regions can be at least partially beneath the slant field plate 28.

In some embodiments, the III-N layer structure in the gate region is different from that in the access regions (not shown). For example, the access regions can include III-N layers that are not included in the gate region, or vice-versa. In some embodiments, the uppermost III-N layer is recessed in the gate region (not shown). The recess in the uppermost III-N layer can extend part way through the layer, such that a portion of the uppermost III-N layer is removed in the gate region. Or, the recess can extend all the way through the uppermost III-N layer and into the III-N layer directly beneath the uppermost III-N layer, such that all of the uppermost III-N layer and a portion of the layer below the uppermost III-N layer are removed in the gate region. Additional examples of III-N layer structures for III-N devices can be found in U.S. Pat. No. 7,915,643, U.S. Pat. No. 7,795,642, U.S. Pat. No. 7,851,825, U.S. Pat. No. 8,519,438, U.S. Pat. No. 7,898,004, U.S. Pat. No. 7,884,394, and U.S. patent application Ser. No. 11/856,695, filed Sep. 17, 2007, all of which are hereby incorporated by reference.

Source and drain electrodes 14 and 15, respectively, which are formed on opposite sides of the gate region, contact the 2DEG channel 19 in channel layer 11. A gate insulator layer 22 is adjacent to the uppermost III-N surface and extends at least from the source electrode 14 to the drain electrode 15. When an uppermost III-N layer is the same layer in both the gate and access regions, as is the case for the device shown in FIG. 5, the uppermost III-N surface refers to the surface of the uppermost III-N layer which is opposite the substrate 10. In some embodiments, an uppermost III-N layer in the gate region is different from that in the access regions, and in these embodiments the uppermost III-N surface includes all surfaces of uppermost III-N layers which are on a side of the device opposite the substrate, including any vertical or angled surfaces that may result from steps, recesses, or discontinuities in uppermost III-N layers.

Gate insulator layer 22 is formed of any insulating film that can be made thin, such as less than about 50 nm, such as less than or about 22 nm, 18 nm, or 15 nm, in order to insure sufficiently high gate capacitance, while preventing substantial current from flowing from the gate 16 to the drain electrode 15 through the 2DEG channel 19. For example, gate insulator layer 22 can be about 2-50 nm thick, can be formed of SiO₂ or SiN, and can be deposited by methods such as chemical vapor deposition (CVD), metalorganic chemical vapor deposition (MOCVD), high-temperature chemical vapor deposition (HTCVD) sputtering, evaporation, or other suitable deposition techniques. In some embodiments, gate insulator layer 22 is formed of a high permittivity (high-K) dielectric such as HfO₂, Ti₂O₅, or ZrO₂. A high-K dielectric results in a higher gate capacitance as compared to the case when a lower permittivity dielectric of the same thickness is used. Consequently, when a high-K dielectric is used, gate insulator layer 22 may not need to be made as thin as when a lower permittivity dielectric is used. For example, when a high-K dielectric is used, it may be possible to achieve a sufficiently large gate capacitance if the thickness of the gate insulator layer is about 2000 nm or less, about 1000 nm or less, or about 500 nm or less.

Gate insulator layer 22 can be made thick enough to prevent substantial leakage currents, i.e., leakage currents greater than about 100 microamperes, from flowing through gate insulator layer 22 during device operation. For example, it may be necessary to make gate insulator layer 22 greater than about 2 nm to substantially suppress leakage currents. In some embodiments, the device is a depletion mode device (i.e., the device threshold voltage is less than 0V), and the thickness of gate insulator layer 22 is chosen such that the device has a threshold voltage of about −30V or greater (i.e., less negative), such as between about −30V and 0 V. The threshold voltage of the device is the maximum voltage at which the 2DEG in the gate region is substantially depleted of charge, i.e., has a charge density less than about 1% of the maximum 2DEG charge density in the device. In other embodiments, the thickness of gate insulator layer 22 is chosen such that the capacitance per unit area of the layer is about 0.8-40 millifarads/meter².

Since gate insulator layer 22 directly contacts the uppermost III-N surface in the device access regions, it can also be capable of serving as an effective surface passivation layer, either on its own or in combination with the overlying layers in the access regions, as will be described below. As used herein, a “passivation layer” refers to any layer or combination of layers grown or deposited on top of uppermost III-N layers in a III-N device which can prevent or suppress voltage fluctuations at the uppermost III-N surface in the access regions during device operation. For example, a passivation layer may prevent or suppress the formation of surface/interface states at the uppermost III-N surface, or it may prevent or suppress the ability of surface/interface states to trap charge during device operation.

In III-N devices, voltage fluctuations at uppermost III-N surfaces, often caused by the charging of surface states during device operation, are known to lead to undesired effects such as dispersion. Dispersion refers to a difference in observed current-voltage (1-V) characteristics when the device is operated under RF or switching conditions as compared to when the device is operated under DC conditions. A thin, e.g., 22 nm, SiN layer deposited by MOCVD has been shown to form a particularly effective gate insulator for III-N devices while simultaneously serving as an adequate passivation layer in the access regions when combined with appropriate overlying layers 21 and 23, as will be described below.

In some implementations, an etch stop layer 21 is formed in the device access regions directly adjacent to gate insulator layer 22, on top of which is formed an electrode defining layer 23. The electrode defining layer 23 has a recess located between the source electrode 14 and drain electrode 15, i.e., in the region between the device access regions. In some embodiments, the etch stop layer 21 is also recessed in this region. An electrode 29 is conformally deposited in the recess. The electrode 29 overlies the gate region and extends towards the drain electrode 15 such that a portion of electrode 29 overlies a portion of electrode defining layer 23. The portion of electrode 29 that overlies the gate region, i.e., is between the two vertical dashed lines, is the gate 16, and the portion of electrode 29 adjacent to gate 16 on a side closest to drain electrode 15 is a slant field plate 28.

As is apparent from FIG. 5, the shape of the slant field plate is in part defined by the shape of the recess, i.e., the profile of sidewall 24 of electrode defining layer 23. As used herein, a “slant field plate” is a field plate for which at least a portion of the underlying surface defining the shape of the field plate is at an angle between about 5 degrees and 85 degrees, such as between about 10 degrees and 70 degrees, relative to the uppermost III-N surface in the gate region. For example, slant field plate 28 in FIG. 5 is defined to be a slant field plate if angle 25 is between about 5 degrees and 85 degrees. Additionally, sidewall 24 does not need to have a linear profile, it can have a profile which is linear, parabolic, or some other shape, as long as at least a substantial portion of sidewall 24 is at an angle of between about 5 degrees and 85 degrees relative to the uppermost III-N surface in the gate region. In some embodiments, the angle of the substantial portion of the underlying surface defining the shape of the field plate, relative to the uppermost III-N surface in the gate region, is between about 30 and 45 degrees.

The portion of electrode defining layer 23 that is on the side of the gate closest to the source electrode 14 can also be sloped in the region adjacent to electrode 29, where the slope in this region is defined by angle 26. The slope in this region can be constant or can vary. In some embodiments, angles 25 and 26 are about the same, whereas in other embodiments they are different. It can be advantageous for the sidewall whose slope is given by angle 26 to be steeper than sidewall 24, as this can reduce the gate-source capacitance. In some embodiments, angle 26 is between about 45 and 90 degrees, such as between about 80 and 90 degrees.

In order to form an electrode defining layer 23 with a sidewall 24 that meets the specifications required for the formation of a slant field plate and simultaneously allow for a gate insulator layer 22 for which the thickness in the region below gate 16 can be controlled with sufficient accuracy, the following fabrication procedures can be used. After deposition or growth of gate insulator layer 22 on a series of III-N layers, etch stop layer 21 is deposited over the entire structure, after which electrode defining layer 23 is deposited everywhere over etch stop layer 21. Next, an etch process with the following properties is used to remove a portion of the material of electrode defining layer 23, which resides above the gate region. The etch process etches the material of electrode defining layer 23 and yields sidewalls such as those described for sidewall 24, but it does not substantially etch the material of etch stop layer 21. In some implementations, the etch process etches the material of electrode defining layer 23 at a substantially higher rate than it etches the material of etch stop layer 21, such as at least about 10 times higher a rate or between about 10 and 10,000 times higher a rate. In other words, the etch process etches electrode defining layer 23 with a selectivity of about 10:1 or higher. In one embodiment, the etch process is a dry etch, such as reactive ion etching (RIE) or inductively coupled plasma etching (ICP), wherein the etch mask includes two layers of photoresist, i.e., a double-layer resist process, where in the unmasked regions the underlying photoresist layer undercuts the overlying photoresist layer. A complete description of this process can be found in the article “HIGH BREAKDOWN VOLTAGE ACHIEVED ON ALGAN/GAN HEMTS WITH INTEGRATED SLANT FIELD PLATES”, published by Dora et al. in IEEE Electron Device Letters, Vol 27, No 9, pp 713-715, which is hereby incorporated by reference throughout. In another embodiment, the etch process is a dry etch, such as reactive ion etching (RIE) or inductively coupled plasma etching (ICP), wherein the photoresist used as an etch mask has a slanted sidewall and can also be etched by the dry etch technique used.

Next, a second etch process with the following properties is used to remove a portion of the material of etch stop layer 21 which resides above the gate region. The second etch process etches the material of etch stop layer 21, but it does not substantially etch the material of gate insulator layer 22. The second etch process may etch the material of etch stop layer 21 at a substantially higher rate than it etches the material of gate insulator layer 22, such as at least about 10 times higher a rate or between about 10 and 10,000 times higher rate. In some embodiments, the second etch process also cannot substantially etch the material of electrode defining layer 23.

Etch stop layer 21 can be formed of an insulating material, such as AlN, SiN, SiO₂, or another insulating material, which has a different composition or is a different material than that of gate insulator layer 22. The different materials or compositions allow for the selectivity of the etching steps. Specifically, etch stop layer 21 can be formed of a material for which an etch process exists that can etch the material of etch stop layer 21 without substantially etching any of the material of gate insulator layer 22. For example, when gate insulator layer 22 is formed of SiN, etch stop layer 21 can be formed of AlN, because a KOH-based wet etch, which does not substantially etch SiN, can be used to etch AlN. Furthermore, if etch stop layer 21 is thin, such as less than about 15 nm, such as about 5 nm, substantial lateral etching of etch stop layer 21 can be prevented. Lateral etching can result in an undercut beneath electrode defining layer 23 in the region adjacent to gate 16. If an undercut is present in this region, then it is possible that the uppermost III-N surface will not be sufficiently passivated in the region directly below the undercut, which can lead to undesirable effects such as dispersion. In some embodiments, etch stop layer 21 is formed of AlN deposited by sputter deposition and is about 5 nm thick.

Electrode defining layer 23 is formed of an insulating material, such as AlN, SiN, or SiO₂, which has a different composition or is a different material than that of etch stop layer 21. The different materials or compositions allow for the selectivity of the etching steps. Specifically, electrode defining layer 23 can be formed of a material for which an etch process exists that can etch the material of electrode defining layer 23 and yield sidewalls such as those described for sidewall 24 while not substantially etching the material of etch stop layer 21. For example, when etch stop layer 21 is formed of AlN, electrode defining layer 23 can be formed of SiN, since a Fluorine-based dry etch exists which etches SiN, does not substantially etch AlN, and can yield sidewalls such as those described for sidewall 24 when an appropriate photoresist etch mask, as previously described, is used. Additionally, in order to optimize the reduction in peak electric field that results from the slant field plate, electrode defining layer 23 can be about 100 nm thick or thicker, such as between about 100 nm and 200 nm thick, such as about 120 nm thick. The optimal thickness for the electrode defining layer 23 depends in part on the operating voltage of the device within the circuit or module in which it is used. For example, if a larger operating voltage is to be used, it may be advantageous to have a thicker electrode defining layer 23, such as between about 200 nm and 2000 nm. In some embodiments, electrode defining layer 23 is formed of SiN deposited by Plasma Enhanced Chemical Vapor Deposition (PECVD) and is about 120 nm thick.

Gate insulator layer 22, etch stop layer 21, and electrode defining layer 23 in combination can form a suitable passivation layer in the device access regions. Gate insulator layer 22, which is adjacent to the uppermost III-N surface, can prevent or suppress the formation of surface/interface states at the uppermost III-N surface, or it can prevent or suppress the ability of surface/interface states to trap charge during device operation. To adequately prevent or suppress dispersion caused by surface/interface states at the uppermost III-N surface, gate insulator layer 22 may need to be about 2 nm thick or thicker. However, making gate insulator layer 22 thicker can reduce the device transconductance, thereby degrading device performance.

To prevent voltage fluctuations at the surface of electrode defining layer 23 on a side opposite the etch stop layer 21 from causing substantial dispersion, the combined thickness of the electrode defining layer 23 and the gate insulator 22 can be sufficiently large, such as about 100 nm thick or thicker. The minimum combined thickness of these two layers that can be required to substantially suppress dispersion depends on the operating voltage (i.e., the maximum voltage difference between the source and drain during operation) of the device. For example, for operation up to about 50 V, the combined thickness can be about 120 nm or thicker, for operation up to about 300 V, the combined thickness can be about 800 nm or thicker, and for operation up to about 600 V, the combined thickness can be about 1800 nm or thicker. Since it can be desirable for the thickness of the gate insulator layer 22 to be small, such as about 20 nm, the thickness of the electrode defining layer 23 can be almost as large as or about the same as the minimum combined thickness of the two layers. Because thick individual layers can be difficult to fabricate, it may be necessary to form additional layers in order to achieve the minimum combined layer thicknesses required to substantially suppress dispersion at higher operating voltages. Such devices are shown in FIGS. 12 a and 13 and are further described below.

In conventional III-N devices, a single SiN layer, that is, a layer that is not used in combination with an etch stop layer or electrode defining layer, of thickness greater than about 30 nm has been shown to be a suitable passivating layer in many cases. A thicker single SiN layer can result in improved passivation, or in effective passivation at higher device operating voltages, as compared to a thinner single SiN layer. For the device of FIG. 5, it has been shown that suitable passivation can be achieved for device operation up to about 50 V when a 2-50 nm MOCVD grown SiN layer is used for gate insulator layer 22, a 1-15 nm AlN layer deposited by sputter deposition is used for etch stop layer 21, and a 100-200 nm SiN layer deposited by PECVD is used for electrode defining layer 23. It has also been shown that increasing the thickness of the etch stop layer 21 can cause the device to experience greater dispersion, thus degrading the device performance. For example, devices were fabricated for which the only parameter which was varied was the thickness of the AlN etch stop layer 21. These devices exhibited increased dispersion for increased thickness of the AlN etch stop layer 21.

A III-N device with a slant field plate and a gate insulator can also be achieved by omitting the etch stop layer 21 in FIG. 5 and choosing a material for the electrode defining layer 23 that can be etched by an etch process that selectively etches the material of electrode defining layer 23 without substantially etching the material of gate insulator layer 22. However, the structure of FIG. 5 may be advantageous as compared to this structure because it can be difficult to find a material for gate insulator layer 22 which serves as a suitable gate insulator for III-N devices while at the same time serving as an etch stop layer for the material of electrode defining layer 23 and simultaneously serving as a suitable passivation layer in conjunction with the material of electrode defining layer 23.

A method of forming the device in FIG. 5 is illustrated in FIGS. 6-11. Referring to FIG. 6, a series of III-N layers which at least includes a channel layer 11 and a barrier layer 12 is formed on a substrate 10, resulting in the formation of a 2DEG 19 in channel layer 11. The III-N layers can be grown epitaxially by a method such as MOCVD, MBE, HVPE, or another method. Next, as seen in FIG. 7, gate insulator layer 22 is formed on top of the series of III-N layers. Gate insulator layer 22 can be grown or deposited by methods such as MOCVD, PECVD, high temperature CVD (HTCVD), sputtering, evaporation, or another method. In some embodiments, gate insulator layer 22 is formed by a similar or the same method as the III-N layers, and can be formed in the same step. For example, the III-N layers and gate insulator layer 22 can all be deposited or grown by MOCVD.

Next, referring to FIG. 8, gate insulator layer 22 is removed in the region containing source and drain electrodes 14 and 15, respectively, and source and drain electrodes 14 and 15, which contact the 2DEG 19, are formed by a method such as evaporation, sputtering, PECVD, HTCVD, or another method. In some embodiments, source and drain electrodes 14 and 15 are formed prior to the formation of gate insulator layer 22.

Referring to FIG. 9, etch stop layer 21 is then formed atop gate insulator layer 22, on top of which is formed electrode defining layer 23. Next, as seen in FIG. 10, an etch mask 17, such as photoresist, is deposited atop electrode defining layer 23 in the regions shown, and electrode defining layer 23 is etched in the unmasked regions using a technique that etches the material of electrode defining layer 23 but does not substantially etch the material of etch stop layer 21. The etching results in slanted sidewalls 24 in the etched region. Thus, the etch can stop precisely at the interface of electrode defining layer 23 and etch stop layer 21. Referring to FIG. 11, etch mask 17 is removed, and etch stop layer 21 is etched in the gate region using a technique that etches the material of etch stop layer 21 but does not substantially etch the material of etch electrode defining layer 23 or of gate insulator layer 22. The etch stop layer has a main surface, which is the surface that interfaces with the electrode defining layer and is exposed when the electrode defining layer is etched through. Thus, the etch can stop precisely at the interface of etch stop layer 21 and gate insulator layer 22. Finally, electrode 29, which includes gate 16 and slant field plate 28, is formed, resulting in the device shown in FIG. 5.

In one embodiment of the device shown in FIG. 5, the III-N layers and gate insulator layer 22 are all grown by MOCVD and are formed in a single growth step. Gate insulator layer 22 includes or is formed of SiN and is about 22 nm thick. Etch stop layer 21 includes or is formed of AlN which is deposited by evaporation or sputtering and is about 5 nm thick. Electrode defining layer 23 includes or is formed of SiN, is deposited by PECVD, and is about 120 nm thick. Etch mask 17, shown in FIG. 10, is photoresist and is patterned in such a way that the sidewall is substantially slanted. Alternatively, the etch mask can be a double-layer photoresist, where the underlying photoresist layer is undercut relative to the overlying photoresist layer. Electrode defining layer 23 is removed in the gate region using a Fluorine-based dry etch, such as RIE or ICP, which etches SiN, does not substantially etch AlN, and yields sidewalls such as those described for sidewall 24 in FIG. 5 when a photoresist with substantially sloped sidewalls or a double-layer photoresist is used as an etch mask. Etch stop layer 21 is removed in the gate region using a KOH-based wet etch which etched AlN but does not substantially etch SiN.

Devices such as the one shown in FIG. 5 with a single field plate have been fabricated for which the dynamic on-resistance (as measured when the device is switched from the OFF state, with a source-drain bias of up to 40V, to the ON state) is no more than 1.2 times the DC on-resistance (R_(ON)). The average DC R_(ON) for a saturation current of 50 mA/mm was found to be about 11.5 ohm-mm, while the average dynamic R_(ON), measured when the device was switched while a source-drain bias of 40V was applied, was found to be about 11.9 ohm-mm. In semiconductor transistors used in switching applications, dispersion can lead to an increase in the dynamic on-resistance of the device. In devices without a slant field plate such as that in the device of FIG. 5, dispersion can lead to dynamic on-resistances that are too large for the application in which the device is being used. Dispersion in the device of FIG. 5 can be kept sufficiently small, i.e., dispersion is substantially suppressed, such that the dynamic on-resistance is acceptable for the device applications.

A schematic diagram of a device which includes a gate insulator and two slant field plates is shown in FIG. 12 a. The device of FIG. 12 a is the same as the one shown in FIG. 5, but further includes an insulator layer 32, a second etch stop layer 31, a second electrode defining layer 33, and an electrode 39 which includes a second slant field plate 38. As compared to the device of FIG. 5, the addition of a second slant field plate 38 can further decrease the peak electric field in the device during device operation, thereby further increasing the device breakdown voltage and decreasing dispersion, or resulting in sufficiently low dispersion at higher voltages than may be possible with the device of FIG. 5.

The second electrode defining layer 33 and second etch stop layer 31 can be similar to those of electrode defining layer 23 and etch stop layer 21, respectively. That is, the second electrode defining layer 33 can be formed of an insulating material, such as AlN, SiN, or SiO₂, which has a different composition or is a different material than that of the second etch stop layer 31. Additionally, the second electrode defining layer 33 can be comprised of a material for which an etch process exists that can etch the material of electrode defining layer 33 and yield slanted sidewalls, such as those described for sidewall 24 in FIG. 5, while not substantially etching the material of the second etch stop layer 31. For example, when the second etch stop layer 31 is AlN, the second electrode defining layer 33 can be SiN, since a Fluorine-based dry etch exists which etches SiN, does not substantially etch AlN, and can yield sidewalls such as those described for sidewall 24 in FIG. 5 when a suitable photoresist etch mask is used. In some embodiments, the second electrode defining layer 33 is between about 10 nm and 1000 nm thick, such as about 500 nm thick. In some embodiments, the second electrode defining layer 33 is formed of SiN deposited by Plasma Enhanced Chemical Vapor Deposition (PECVD) and is about 500 nm thick.

The second etch stop layer 31 can be formed of an insulating material, such as AlN, SiN, or SiO₂, which has a different composition or is a different material than that of the underlying insulator layer 32 and different from that of the second electrode defining layer 33. The second etch stop layer 31 can be comprised of a material for which an etch process exists that can etch the material of etch stop layer 31 without substantially etching any of the material of the underlying insulator layer 32 or of the second electrode defining layer 33. For example, when the underlying insulator layer 32 and the second electrode defining layer 33 are SiN, the second etch stop layer 31 can be AlN, since a KOH-based wet etch which does not substantially etch SiN can be used to etch AlN. Furthermore, the second etch stop layer 31 can be thin, such as less than about 15 nm, such as about 5 nm thick, in order to prevent substantial lateral etching of the second etch stop layer 31 that can result in an undercut beneath the second electrode defining layer 33. In some embodiments, the second etch stop layer 31 is formed of AlN deposited by sputter deposition and is about 5 nm thick.

A method of forming electrode 39 and the adjacent layers in the device of FIG. 12 a is similar or the same to that described for the formation of the electrode 29 and the adjacent layers in the device of FIG. 5. Additionally, electrode 39 and electrode 29 (labeled in FIG. 5 but not in FIG. 12 a for convenience) can be electrically connected, either externally or on the device periphery, such that the second slant field plate 38 is a gate-connected field plate (not shown). As used herein, two or more contacts or other items are said to be “electrically connected” if they are connected by a material which is sufficiently conducting to ensure that the electric potential at each of the contacts or other items is intended to be the same, i.e., is about the same, at all times. Furthermore, additional slant field plates, which can also be gate-connected field plates, can be added to this device using a similar or the same process and structure described for electrode 39 and the adjacent layers.

Insulator layer 32, which can be SiN, separates electrode 39 from electrode 29 and can protect electrode 29 from being damaged when the second etch stop layer 31 is etched. In some embodiments, insulator layer 32 is not included, in which case electrode 39 can be directly connected to electrode 29 within the active device area.

In one embodiment of the device shown in FIG. 12 a, the III-N layers and gate insulator layer 22 are all grown by MOCVD and are formed in a single growth step. Gate insulator layer 22 is SiN and is about 22 nm thick. Etch stop layer 21 includes or is formed of AlN, deposited by evaporation or sputtering, and is about 5 nm thick. Electrode defining layer 23 is SiN, deposited by PECVD, and is about 120 nm thick. Etch mask 17, shown in FIG. 10, is formed of photoresist and is patterned in such a way that the sidewall is either substantially slanted or has an undercut so that a trench with slant sidewalls can be defined in the underlying electrode defining layer 23. Electrode defining layer 23 is removed in the gate region using a Fluorine-based dry etch, such as RIE or ICP, which etches SiN, does not substantially etch AlN, and yields sidewalls such as those described for sidewall 24 in FIG. 5 when a suitable photoresist etch mask is used. Etch stop layer 21 is removed in the gate region using a KOH-based wet etch which etched AlN but does not substantially etch SiN. Insulator layer 32 is SiN, deposited by PECVD, and is about 200 nm thick. The second etch stop layer 31 is AlN, deposited by evaporation or sputtering, and is about 5 nm thick. The second electrode defining layer 33 is SiN, deposited by PECVD, and is about 500 nm thick. The second electrode defining layer 33 is etched using a Fluorine-based dry etch, such as RIE or ICP, which etches SiN, does not substantially etch AlN, and yields sidewalls such as those described for sidewall 24 in FIG. 5 when a suitable photoresist etch mask is used. The second etch stop layer 31 is etched using a KOH-based wet etch which etches AlN but does not substantially etch SiN.

Devices such as the one shown in FIG. 12 a with two slant field plates have been fabricated for which the dynamic on-resistance (as measured when the device is switched from the OFF state, with a source-drain bias of up to 200 V, to the ON state) is no more than 1.2 times the DC on-resistance (R_(ON)). The average DC R_(ON) for a saturation current of 50 mA/mm was found to be about 11.5 ohm-mm, while the average dynamic R_(ON), measured when the device was switched while a source-drain bias of 200V was applied, was also found to be about 11.5 ohm-mm. In semiconductor transistors used in switching applications, dispersion can lead to an increase in the dynamic on-resistance of the device. In devices without multiple slant field plates such as those in the device of FIG. 12 a, dispersion can lead to dynamic on-resistances that are too large for the application in which the device is being used. Dispersion in the device of FIG. 12 a can be kept sufficiently small, i.e., dispersion is substantially suppressed, such that the dynamic on-resistance is acceptable for the device applications.

Devices similar to the one shown in FIG. 12 a, but with three slant field plates, have been fabricated for which the dynamic on-resistance (as measured when the device is switched from the OFF state, with a source-drain bias of up to 600 V, to the ON state) is no more than 1.2 times the DC on-resistance (R_(ON)). A graph showing average R_(ON) versus drain voltage V_(d) for these devices is shown in FIG. 12 b. The average DC R_(ON) for these devices was about 170 milli-ohms, while the average dynamic R_(ON), measured when the device was switched from the OFF state, with a source-drain bias of 600 V, to the ON state, was found to be about 200 milli-ohms.

Devices similar to the one shown in FIG. 12 a, but with four slant field plates, have been fabricated for which the dynamic on-resistance (as measured when the device is switched from the OFF state, with a source-drain bias of up to 800 V, to the ON state) is no more than 1.4 times the DC on-resistance (R_(ON)). A graph showing average R_(ON) versus drain voltage V_(d) for these devices is shown in FIG. 12 c. The average DC R_(ON) for these devices was about 1000 milli-ohms, while the average dynamic R_(ON), measured when the device was switched from the OFF state, with a source-drain bias of 800 V, to the ON state, was found to be about 1400 milli-ohms.

Another device, which includes a gate insulator 22 and two slant field plates 28 and 38, is shown in FIG. 13. This device is similar to the one shown in FIG. 12, except that the two slant field plates 28 and 38 are connected to one another in the active device area and can be formed with a single metal deposition. For example, electrode 49, which includes the device gate 16 as well as slant field plates 28 and 38, can be deposited in a single step. This can be advantageous as compared to the device of FIG. 12 a, since the manufacturing process can be simplified and the gate resistance may be reduced.

Electrode 49 and the layers adjacent to electrode 49 in the device of FIG. 13 can be formed as follows. Gate insulator layer 22, first etch stop layer 21, first electrode defining layer 23, second etch stop layer 31, and second electrode defining layer 33 are all deposited above the active semiconductor device layers. An etch mask, such as photoresist, is then patterned on top of layer 33, and an aperture is etched in layer 33 using an etch process which does not etch the material of layer 31 and results in slanted sidewalls in layer 33, as previously described. The portion of layer 31 adjacent to the aperture is then etched using a process which etches the material of layer 31 but not that of layers 33 or 23. The etch mask which was deposited and patterned on top of layer 33 is removed, either before or after the etching of layer 33. Next, a second etch mask, such as photoresist, is deposited over the device such that the exposed surfaces of layers 33 and 31, as well as the exposed portion of layer 23 outside of region 59, are covered by the etch mask material, but the exposed portion of layer 23 with region 59 is not covered by the etch mask material. Next, an aperture is etched in layer 23 using an etch process which does not etch the material of layer 21 and results in slanted sidewalls in layer 23, as previously described. Finally, the second etch mask is removed, and the portion of layer 21 adjacent to the aperture in layer 23 is etched using a process which etches the material of layer 21 but not that of layers 22 or 23.

A diode which includes a slant field plate 28 is shown in FIGS. 14 and 15, where FIG. 14 is a cross-sectional view and FIG. 15 is a plan view of the device. The plan view shown in FIG. 15 illustrates the layouts of anode and cathode contacts 61 and 60, respectively. While the anode and cathode contacts on FIG. 15 are shown to be circular in shape, they can in general be any shape appropriate for the layout of the circuit in which they are used. The diode includes III-N channel and barrier layers 11 and 12, which contain a 2DEG channel 19 and are similar to the III-N layers in the device of FIG. 5. Anode contact 61 is formed of a single electrode or a plurality of electrodes and directly contacts the underlying semiconductor materials. Cathode contact 60 contacts the 2DEG channel 19 and is in close proximity to at least a portion of anode contact 61. Cathode contact 60 is an ohmic contact, or exhibits substantially ohmic behavior, and anode contact 61 is a Schottky contact or forms a substantially Schottky contact to the underlying III-N layers. Cathode contact 60 can be a single cathode contact. As used herein, the term “single cathode contact” refers to either a single metallic contact which serves as a cathode, or to a plurality of contacts serving as cathodes which are electrically connected such that the electric potential at each contact is about the same. Anode and cathode contacts 61 and 60 may be any arbitrary shape, although the shape is ideally optimized to minimize the device area required for a given forward current.

Dielectric layer 62 is formed of an insulator or dielectric and is adjacent to the uppermost III-N surface in the device access regions. Dielectric layer 62 is capable of serving as an effective surface passivation layer, either on its own or in combination with the overlying layers in the access regions. Layer 21 is an etch stop layer, and layer 23 is an electrode defining layer, with similar or the same requirements as those of the etch stop and electrode defining layers, respectively, in the device of FIG. 5.

The diode in FIGS. 14 and 15 operates as follows. When the voltage at the anode contact 61 is less than that at the cathode contact 60, such that the Schottky junction between anode contact 61 and III-N layer 12 is reverse biased, the diode is in the OFF state with no substantial current flowing between the anode and cathode. When the voltage at the anode contact 61 is greater than that at the cathode contact 60, the Schottky junction between anode contact 61 and III-N layer 12 is forward biased, and the diode is in the ON state. Electrons flow from the cathode contact 60 predominantly through the 2DEG channel 19 and then through the forward biased Schottky junction into the anode contact 61. That is, at least 99% of the total forward bias current flows from the anode to the cathode through the Schottky barrier and through the 2DEG channel. A small amount of leakage current can flow through other paths, such as along the surface of the device.

The device in FIG. 16 is similar to that of FIG. 14, except that in the anode region 64, the III-N materials are recessed all the way through III-N barrier layer 12 and part way through III-N channel layer 11, such that the recess extends through the region which contained the 2DEG. In this case, anode contact 61 forms a substantially Schottky contact to some or all of the III-N layers which it directly contacts. In some embodiments, the recess only extends part way through III-N layer 12 and does not extend through the region containing the 2DEG channel (not shown). During reverse bias operation, the portion of 2DEG channel 19 directly underneath portion 66 of the anode contact, i.e., the portion of the anode contact directly overlying and adjacent to dielectric layer 62, can be depleted of electrons, thereby reducing reverse leakage currents in the device. The portion of 2DEG channel 19 directly underneath portion 66 of the anode contact is the portion of 2DEG channel in the device access region, i.e., the region between anode region 64 and the cathode contact 60, and limited to a region adjacent to anode region 64. In order for the portion of 2DEG channel 19 directly underneath portion 66 of the anode contact to become depleted of electrons during reverse bias operation, dielectric layer 62 cannot be too thick. In some embodiments, dielectric layer 62 is silicon nitride and is less than about 50 nm, such as between about 2 nm and 50 nm. Dielectric layer 62 can be made thick enough to prevent substantial leakage currents, i.e., leakage currents greater than about 10 microamperes/millimeter, from flowing from the anode to the cathode through dielectric layer 62 in the region directly underneath portion 66 of the anode contact. For example, it may be necessary to make dielectric layer 62 greater than about 2 nm to substantially suppress leakage currents. In some embodiments, the thickness of dielectric layer 62 is chosen such that in the region directly underneath portion 66 of the anode contact, the device has a threshold voltage of about −15V or greater (i.e., less negative or more positive), such as between about −15V and −1V. The threshold voltage of the region directly underneath portion 66 of the anode contact is the maximum voltage at which the 2DEG in this region is substantially depleted of charge, i.e., has a charge density less than about 1% of the maximum 2DEG charge density in the device. In other embodiments, the thickness of gate insulator layer 22 is chosen such that the capacitance per unit area of the layer is about 0.8-40 millifarads/m². In some embodiments, dielectric layer 62 is SiN and is deposited by metal-organic chemical vapor deposition (MOCVD).

If dielectric layer 62 is a higher K dielectric than silicon nitride, the dielectric layer can be thicker. For example, it may be possible to achieve the desired threshold voltage in the region directly underneath portion 66 of the anode contact by using a high K dielectric for dielectric layer 62 that is thicker than a SiN layer designed to result in the same threshold voltage for this region.

Other features which are well known to be beneficial to device performance can also be included in the structures in FIGS. 5, 12 a, and 13-16. These include but are not limited to surface treatments to the III-N layers in the gate and/or access regions, or inclusion of a III-N buffer layer, such as a III-N layer with a larger bandgap than that of the channel layer 11, between the channel layer 11 and substrate 10. The semiconductor layers do not need to be III-N layers, but can instead be formed of other semiconductor materials. The field plates do not need to be slant field plates, but can instead be other types of field plates. These features can be used individually or in combination with one another. 

What is claimed is:
 1. A method of forming a III-N device, comprising: providing a III-N material layer; forming an insulator layer on a surface of the III-N material layer; forming a first etch stop layer on an opposite side of the insulator layer from the III-N material layer; forming a first electrode defining layer on an opposite side of the first etch stop layer from the insulator layer; forming an electrode, wherein a recess is formed in the first electrode defining layer and the electrode is formed in the recess; and forming a stack on an opposite side of the first electrode defining layer from the first etch stop layer, wherein the stack comprises a second etch stop layer and a second electrode defining layer.
 2. The method of claim 1, wherein the recess is also formed through the second electrode defining layer and through the second etch stop layer, and a portion of the electrode is on an opposite side of the second electrode defining layer from the first electrode defining layer.
 3. The method of claim 2, wherein the recess is also formed through the first etch stop layer.
 4. The method of claim 3, wherein the recess is also formed through the insulator layer.
 5. The method of claim 4, wherein the recess extends into the III-N material layer, and the electrode is in a portion of the recess in the III-N material layer.
 6. The method of claim 5, a first portion of the III-N material layer having a first composition and a second portion of the III-N material layer having a second composition, wherein a difference between the first composition and the second composition forms a 2DEG channel in the III-N material layer.
 7. The method of claim 6, wherein the recess extends through the 2DEG channel.
 8. The method of claim 1, further comprising forming a second insulator layer between the first electrode defining layer and the second etch stop layer.
 9. The method of claim 8, further comprising forming a second recess in the second electrode defining layer and in the second etch stop layer, and forming a second electrode in the second recess.
 10. The method of claim 9, wherein the second electrode is electrically connected to the first electrode.
 11. The method of claim 1, further comprising forming one or more additional stacks, wherein a recess is formed in each stack, and an electrode is formed in each recess. A III-N device, comprising: a III-N material layer; an insulator layer on a surface of the III-N material layer, the insulator layer comprising SiN or SiO2; an etch stop layer on an opposite side of the insulator layer from the III-N material layer; an electrode defining layer on an opposite side of the etch stop layer from the insulator layer; a first electrode, wherein a recess is formed in the electrode defining layer and the first electrode is formed in the recess; and a second electrode on the III-N material layer, wherein the insulator layer extends at least to and contacts the second electrode.
 12. The method of claim 1, wherein a portion of the recess in the first electrode defining layer has angled walls with at least a portion that is at a non-perpendicular angle to a main surface of the first etch stop layer.
 13. The method of claim 12, wherein the non-perpendicular angle is between 5 degrees and 85 degrees.
 14. The method of claim 1, wherein the first etch stop layer and the insulator layer are formed of different materials.
 15. The method of claim 14, wherein the first etch stop layer is formed of aluminum nitride, and the insulator layer is formed of silicon nitride.
 16. The method of claim 1, a first portion of the III-N material layer having a first composition and a second portion of the III-N material layer having a second composition, wherein a difference between the first composition and the second composition forms a 2DEG channel in the III-N material layer.
 17. The method of claim 1, wherein the recess is also formed through the first etch stop layer.
 18. The method of claim 1, wherein the device is a transistor, the electrode is a gate electrode, and the device further comprises a source and a drain.
 19. The method of claim 1, wherein the electrode includes a field plate.
 20. A method of forming a III-N transistor, comprising: providing a III-N material layer; forming an insulator layer on a surface of the III-N material layer; forming etch stop layer on an opposite side of the insulator layer from the III-N material layer; forming an electrode defining layer on an opposite side of the etch stop layer from the insulator layer; and forming an electrode, wherein a recess is formed in the electrode defining layer and the electrode is formed in the recess, the electrode including a field plate; wherein a dynamic on-resistance of the transistor, as measured when the transistor is switched from the OFF state, with an OFF state source-drain bias of about 800 V, to the ON state, is equal to or less than 1.4 times a DC on-resistance of the transistor. The device of claim 1, wherein the recess is formed in the etch stop layer.
 21. The method of claim 20, wherein the recess is also formed through the etch stop layer.
 22. The method of claim 20, wherein the etch stop layer is formed of aluminum nitride, and the insulator layer is formed of silicon nitride.
 23. A method of forming a III-N device, comprising: a providing a III-N material layer; forming an insulator layer on a surface of the III-N material layer; forming an etch stop layer on an opposite side of the insulator layer from the III-N material layer; forming an electrode defining layer on an opposite side of the etch stop layer from the insulator layer, wherein a recess having a first sidewall and a second sidewall is formed in the electrode defining layer, the first sidewall being on an opposite side of the recess from the second sidewall, the first and second sidewalls each extending from a first surface of the electrode defining layer to a second surface of the electrode defining layer, the first surface being adjacent to the etch stop layer and the second surface being opposite the first surface; forming a gate electrode in the recess and over the first and second sidewalls; forming a source; and forming a drain on an opposite side of the recess from the source, the source being proximal to the first sidewall and the drain being proximal to the second sidewall; wherein a first angle is formed between a surface of the etch stop layer and a portion of the first sidewall, the portion of the first sidewall being adjacent to the surface of the etch stop layer; a second angle is formed between the surface of the etch stop layer and a portion of the second sidewall, the portion of the second sidewall being adjacent to the surface of the etch stop layer; and the first angle is greater than the second angle.
 24. The method of claim 23, the first angle being substantially greater than the second angle, wherein a gate-source capacitance of the device is reduced as compared to a similar device in which the first angle is about the same as the second angle.
 25. The method of claim 23, wherein the second angle is between 30 and 45 degrees.
 26. The method of claim 25, wherein the first angle is between 45 and 90 degrees.
 27. The method of claim 23, a first portion of the III-N material layer having a first composition and a second portion of the III-N material layer having a second composition, wherein a difference between the first composition and the second composition forms a 2DEG channel in the III-N material layer.
 28. The method of claim 23, wherein the recess is formed in the etch stop layer.
 29. A method of forming a III-N transistor, comprising: providing a III-N material layer; forming an insulator layer on a surface of the III-N material layer; forming an etch stop layer on an opposite side of the insulator layer from the III-N material layer; forming an electrode defining layer on an opposite side of the etch stop layer from the insulator layer; forming a recess in the electrode defining layer, the recess having a sidewall; and forming an electrode in the recess, a first portion of the electrode being formed over the sidewall; wherein a dynamic on-resistance of the transistor as measured when the transistor is switched from the OFF state, with a source-drain bias of 600 V, to the ON state, is no more than 1.2 times a DC on-resistance of the transistor.
 30. The method of claim 29, wherein the first portion of the electrode comprises a first slant field plate and a second slant field plate.
 31. The method of claim 30, wherein a second portion of the electrode is a gate.
 32. The method of claim 31, wherein the first slant field plate is between the second slant field plate and the gate.
 33. The method of claim 31, further comprising forming a drain on the III-N material layer, wherein the first slant field plate and the second slant field plate are between the gate and the drain.
 34. The method of claim 29, a first portion of the III-N material layer having a first composition and a second portion of the III-N material layer having a second composition, wherein a difference between the first composition and the second composition forms a 2DEG channel in the III-N material layer.
 35. The method of claim 29, wherein the recess is formed in the etch stop layer.
 36. A method of forming a device, comprising: applying an insulator layer on a surface of a III-N material layer; applying a first etch stop layer on the insulator layer; applying a first electrode defining layer on the first etch stop layer; applying a stack on an opposite side of the first electrode defining layer from the first etch stop layer, wherein the stack comprises a second etch stop layer and a second electrode defining layer; etching a recess through the stack and through the first electrode defining layer; and depositing a conductive material in the recess.
 37. The method of claim 36, further comprising etching the first etch stop layer to extend the recess to the insulator layer.
 38. The method of claim 37, wherein the recess is further etched through the insulator layer.
 39. The method of claim 36, wherein the recess is defined at least in part by a wall that is not perpendicular to a surface of the first etch stop layer.
 40. The method of claim 36, wherein the etching step uses an etchant that is selective to etching the first electrode defining layer at a faster rate than the first etch stop layer.
 41. The method of claim 36, wherein a portion of the conductive material is on an opposite side of the second electrode defining layer from the first electrode defining layer. 